Description of corundum refractory brick
Corundum refractory brick refers to refractory brick products with Al2O3 content more than 90%. The raw material used is a solid solution synthesized by melting alumina and chromium oxide in a certain proportion at high temperature. Refractory bricks are made by the production process of special refractory materials.
Advantages of corundum refractory brick
Corundum refractory brick has high temperature resistance, good chemical stability and strong resistance to acid or alkaline slag, metal and glass liquid.
Application of corundum refractory brick
Corundum refractory brick is mainly used for ironmaking blast furnace and blast furnace hot blast furnace, steel refining furnace outside the furnace, sliding water heater, glass furnace and petrochemical industrial furnace.
More refractory product: High Aluminate Wear Resistant Castable
Corundum refractory brick index:
| ltem | Ultra Purity Corundum Brick | 99 Corundum Brick | 90 Corundum Brick | Corundum-Mullite Brick |
| Al2O3% | ≥99.3 | ≥98.5 | ≥90 | ≥80 |
| SiO2% | ≤0.15 | ≤0.3 | ≤8.5 | ≤18.5 |
| Fe2O3% | ≤0.1 | ≤0.2 | ≤0.2 | ≤0.3 |
| Bulk density, g/cm3 | ≥3.25 | ≥3.25 | ≥3.1 | ≥2.9 |
| Apparent porosity, % | ≤18 | ≤18 | ≤18 | ≤18 |
| Cold crushing strength, MPa | ≥100 | ≥100 | ≥120 | ≥120 |
| Refractoriness under load, ℃(0.2MPa,0.6%) | ≥1700 | ≥1700 | ≥1700 | ≥1700 |
| Reheating linear change rate, %(1600℃ x 8h) | -0.2 | -0.2 | 0.2 | 0.2 |
| Thermal expansion coefficient, x 10-6 (Room temp. to 1300'C) | 8.1 | 8.1 | 8.1 | 7.6 |
Azs zircon corundum bricks index:
| ltem | AZS-33 | AZS-33 | AZS-36 | AZS-36 | AZS-41 | AZS-41 |
| Y | H | Y | H | Y | H | |
| Al2O3≥ | 90 | 90 | 90 | 90 | 90 | 90 |
| ZrO2≥ | 32.0 | 32.0 | 35.0 | 35.0 | 40.0 | 40.0 |
| SiO2≤ | 16.0 | 17.0 | 13.5 | 14.5 | 13.0 | 14.0 |
| Na2O≤ | 1.5 | 1.5 | 1.4 | 1.4 | 1.3 | 1.3 |
| Fe2O3+TiO2+CaO+MgO +Na2O+K2O+B2O3≤ | 2.5 | 3.0 | 2.5 | 3.0 | 2.5 | 3.0 |
| BD, PT.QX ≥ | 3.40 | 3.30 | 3.45 | 3.40 | 3.55 | 3.50 |
| BD, MS≤ | 3.50 | 3.45 | 3.60 | 3.55 | 3.70 | 3.65 |
| BD, WS≤ | 3.60 | 3.55 | 3.70 | 3.65 | 3.80 | 3.75 |
Note: PT - ordinary pouring products; QX - inclined pouring products; MS - dense pouring products; Ws - keyless casting.